A glass ionomer cement is a dental restorative material used in dentistry as a filling material and luting cement, including for orthodontic bracket attachment. Glass-ionomer cements are based on the reaction of silicate glass-powder (calciumaluminofluorosilicate glass)and polyacrylic acid, an ionomer. Occasionally water is used instead of an acid, altering the properties of the material and its uses. This reaction produces a powdered cement of glass particles surrounded by matrix of fluoride elements and is known chemically as glass polyalkenoate. There are other forms of similar reactions which can take place, for example, when using an aqueous solution of acrylic/itaconic copolymer with Tartaric acid, this results in a glass-ionomer in liquid form. An aqueous solution of maleic acid polymer or maleic/acrylic copolymer with tartaric acid can also be used to form a glass-ionomer in liquid form. Tartaric acid plays a significant part in controlling the setting characteristics of the material. Glass-ionomer based hybrids incorporate another dental material, for example resin-modified glass ionomer cements (RMGICs) and compomers (or modified composites).
Video Glass ionomer cement
Background
Glass ionomer cement is primarily used in the prevention of dental caries. This dental material has good adhesive bond properties to tooth structure, allowing it to form a tight seal between the internal structures of the tooth and the surrounding environment. Dental caries is caused by bacterial production of acid during their metabolic actions. The acid produced from this metabolism results in the breakdown of tooth enamel and subsequent inner structures of the tooth, if the disease is not intervened by a dental professional, or if the carious lesion does not arrest and/or the enamel re-mineralises by itself. Glass ionomer cements act as sealants when pits and fissures in the tooth occur and release fluoride to prevent further enamel demineralisation and promote remineralisation. Fluoride can also hinder bacterial growth, by inhibiting their metabolism of ingested sugars in the diet. It does this by inhibiting various metabolic enzymes within the bacteria. This leads to a reduction in the acid produced during the bacteria's digestion of food, preventing a further drop in pH and therefore preventing carious.
The application of glass ionomer sealants to occlusal surfaces of the posterior teeth, reduce dental caries in comparison to not using sealants at all. There is evidence that when using sealants, only 6% of people develop tooth decay over a 2-year period, in comparison to 40% of people when not using a sealant. However, it is recommended that the use of fluoride varnish alongside glass ionomer sealants should be applied in practice to further reduce the risk of secondary dental caries.
However, the addition of resin to glass ionomers, improves properties significantly, allowing it to be more easily mixed and placed. Resin-modified glass ionomers allow equal or higher fluoride release and there is evidence of higher retention, higher strength and lower solubility. Resin-based glass ionomers have two setting reactions: an acid-base setting and a free-radical polymerisation. The free-radical polymerisation is the predominant mode of setting, as it occurs more rapidly than the acid-base setting, which is comparatively slower. Only the material properly activated by light will be optimally cured. The presence of resin protects the cement from water contamination. Due to the shortened working time, it is recommended that placement and shaping of the material occurs as soon as possible after mixing.
Maps Glass ionomer cement
History
Dental sealants were first introduced as part of the preventative programme, in the late 1960s, in response to increasing cases of pits and fissures on occlusal surfaces due to caries. This led to glass ionomer cements to be introduced in 1972 by wilson and kent as derivative of the silicate cements and the polycarboxylate cements. The glass ionomer cements incorporated the fluoride releasing properties of the silicate cements with the adhesive qualities of polycarboxylate cements. This incorporation allowed the material to be stronger, less soluble and more translucent (and therefore more aesthetic) than its predecessors.
Glass ionomer cements were initially intended to be used for the aesthetic restoration of anterior teeth and were recommended for restoring Class III and Class V cavity preparations. There have now been further developments in the material's composition to improve properties. For example, the addition of metal or resin particles into the sealant is favoured due to the longer working time and the material being less sensitive to moisture during setting.
When glass ionomer cements were first used, they were mainly used for the restoration of abrasion/erosion lesions and as a luting agent for crown and bridge reconstructions. However, this has now been extended to occlusal restorations in deciduous dentition, restoration of proximal lesions and cavity bases and liners. This is made possible by the ever-increasing new formulations of glass ionomer cements.
Glass ionomer versus resin-based sealants
When the two dental sealants are compared, there has always been a contradiction as to which materials is more effective in caries reduction. Therefore, there are claims against replacing resin-based sealants, the current Gold Standard, with glass ionomer.
Advantages
Glass ionomer sealants are thought to prevent caries through a steady fluoride release over a prolonged period and the fissures are more resistant to demineralization, even after the visible loss of sealant material.
These sealants have hydrophilic properties, allowing them to be an alternative of the hydrophobic resin in the generally wet oral cavity. Resin-based sealants are easily destroyed by saliva contamination.
Chemically curable glass ionomer cements are considered safe from allergic reactions but a few have been reported with resin-based materials. Nevertheless, allergic reactions are very rarely associated with both sealants.
Disadvantages
The main disadvantage of glass ionomer sealants or cements has been inadequate retention or simply lack of strength, toughness, and limited wear resistance. For instance, due to its poor retention rate, periodic recalls are necessary, even after 6 months, to eventually replace the lost sealant. Different methods have been used to address the physical shorcomings of the glass ionomer cements such as thermo-light curing(polymerization), or addition of the zirconia, hydroxyapatite, N-vinyl pyrrolidone, N-vinyl caprolactam, and fluoroapatite to reinforce the glass ionomer cements.
Clinical applications
Glass ionomers are used frequently due to the versatile properties they contain and the relative ease with which they can be used. Prior to procedures, starter materials for glass ionomers are supplied either as a powder and liquid or as a powder mixed with water. A mixed form of these materials can be provided in an encapsulated form.
Preparation of the material should involve following manufacture instructions. A paper pad or cool dry glass slab may be used for mixing the raw materials though it is important to note that the use of the glass slab will retard the reaction and hence increase the working time. The raw materials in liquid and powder form should not be dispensed onto the chosen surface until the mixture is required in the clinical procedure the glass ionomer is being used for, as a prolonged exposure to the atmosphere could interfere with the ratio of chemicals in the liquid. At the stage of mixing, a spatula should be used to rapidly incorporate the powder into the liquid for a duration of 45-60 seconds depending on manufacture instructions and the individual products.
Once mixed together to form a paste, an acid-base reaction occurs which allows the glass ionomer complex to set over a certain period of time and this reaction involves four overlapping stages:
- Dissolution
- Gelation
- Hardening (3-6 min)
- Maturation (24 hr - 1 yr)
It is important to note that glass ionomers have a long setting time and need protection from the oral environment in order to minimize interference with dissolution and prevent contamination.
The type of application for glass ionomers depends on the cement consistency as varying levels of viscosity from very high viscosity to low viscosity, can determine whether the cement is used as luting agents, orthodontic bracket adhesives, pit and fissure sealants, liners and bases, core build-ups, or intermediate restorations.
Clinical uses
The different clinical uses of glass ionomer compounds as restorative materials include;
- Cermets, which are essentially metal reinforced, glass ionomer cements, used to aid in restoring tooth loss as a result of decay or cavities to the tooth surfaces near the gingival margin, or the tooth roots, though cermets can be incorporated at other sites on various teeth, depending on the function required. They maintain adhesion to enamel and dentine and have an identical setting reaction to other glass ionomers.The development of cermets is an attempt to improve the mechanical properties of glass ionomers, particularly brittleness and abrasion resistance by incorporating metals such as silver, tin, gold and titanium. The use of these materials with glass ionomers appears to increase the value of compressive strength and fatigue limit as compared to conventional glass ionomer, however there is no marked difference in the flexural strength and resistance to abrasive wear as compared to glass ionomers.
- Dentine surface treatment, which can be performed with glass ionomer cements as the cement has adhesive characteristics which may be useful when placed in undercut cavities. The surfaces on which the glass cement ionomers are placed would be adequately prepared by removing the precipitated salivary proteins, present from saliva as this would greatly reduce the receptiveness of the glass ionomer cement and dentine surface, to bond formation. A number of different substances can be used to remove this element, such as citric acid, however the most effective substance seems to be poly(acrylic) acid, which is applied to the tooth surface for 30 seconds before it is washed off. The tooth is then dried to ensure the surface is receptive to bond formation but care is taken to ensure desiccation does not occur.
- Matrix techniques with glass ionomers, which are used to aid in proximal cavity restorations of anterior teeth. Between the teeth that are adjacent to the cavity, the matrix is inserted, commonly before any dentine surface conditioning. Once the material is inserted in excess, the matrix is placed around the tooth root and kept in place with the help of firm digital pressure while the material sets. Once set, the matrix can be carefully removed using a sharp probe or excavator.
- Fissure sealants, which involve the use of glass ionomers as the materials can be mixed to achieve a certain fluid consistency and viscosity that allows the cement to sink into fissures and pits located in posterior teeth and fill these spaces which pose as a site for caries risk, thereby reducing the risk of caries manifesting.
- Orthodontic brackets, which can involve the use of glass ionomer cements as an adhesive cement that forms strong chemical bonds between the enamel and the many metals which are used in orthodontic brackets such as stainless steel.
- Fluoride varnishes have been combined with sealant application in the prevention of dental caries. It has been proven that the combined usage of both increases the overall effectiveness as compared to using fluoride varnish alone.
Chemistry and setting reaction
All GICs contain a basic glass and an acidic polymer liquid, which set by an acid-base reaction. The polymer is an ionomer, containing a small proportion - some 5 to 10% - of substituted ionic groups. These allow it to be acid decomposable and clinically set readily.
The glass filler is generally a calcium alumino fluorosilicate powder, which upon reaction with a polyalkenoic acid gives a glass polyalkenoate-glass residue set in an ionised, polycarboxylate matrix.
The acid base setting reaction begins with the mixing of the components. The first phase of the reaction involves dissolution. The acid begins to attach the surface of the glass particles, as well as the adjacent tooth substrate, thus precipitating their outer layers but also neutralising itself. As the pH of the aqueous solution rises, the polyacrylic acid begins to ionise, and becoming negatively charged it sets up a diffusion gradient and helps draw cations out of the glass and dentine. The alkalinity also induces the polymers to dissociate, increasing the viscosity of the aqueous solution.
The second phase is gelation, where as the pH continues to rise and the concentration of the ions in solution to increase, a critical point is reached and insoluble polyacrylates begin to precipitate. These polyanions have carboxylate groups whereby cations bind them, especially Ca2+ in this early phase, as it is the most readily available ion, crosslinking into calcium polyacrylate chains that begin to form a gel matrix, resulting in the initial hard set, within five minutes. Crosslinking, H bonds and physical entanglement of the chains are responsible for gelation. During this phase, the GIC is still vulnerable and must be protected from moisture. If contamination occurs, the chains will degrade and the GIC lose its strength and optical properties. Conversely, dehydration early on will crack the cement and make the surface porous.
Over the next twenty four hours maturation occurs. The less stable calcium polyacrylate chains are progressively replaced by aluminium polyacrylate, allowing the calcium to join the fluoride and phosphate and diffuse into the tooth substrate, forming polysalts, which progressively hydrate to yield a physically stronger matrix.
The incorporation of fluoride delays the reaction, increasing the working time. Other factors are the temperature of the cement, and the powder to liquid ratio - more powder or heat speeding up the reaction.
GICs have good adhesive relations with tooth substrates, uniquely chemically bonding to dentine and, to a lesser extend, to enamel. During initial dissolution, both the glass particles and the hydroxyapatite structure are affected, and thus as the acid is buffered the matrix reforms, chemically welded together at the interface into a calcium phosphate polyalkenoate bond. In addition, the polymer chains are incorporated into both, weaving cross links, and in dentine the collagen fibres also contribute, both linking physically and H-bonding to the GIC salt precipitates. There is also microretention from porosities occurring in the hydroxyapatite.
References
Further reading
- Anusavice, Kenneth J.; Ralph W. Phillips; Chiayi Shen; H. Ralph Rawls (2013). Phillips' Science of Dental Materials (12th ed.). St. Louis, Mo.: Elsevier/Saunders. ISBN 978-1-4377-2418-9. OCLC 785080357.
- McCabe, John F.; Angus W. G. Walls (2008). Applied Dental Materials (9th ed.). Oxford, UK: Blackwell Publishing. ISBN 978-1-4051-3961-8. OCLC 180080871. Retrieved 28 March 2013.
- Van Noort, Richard (2013). "2.3 Glass-ionomer cements and resin-modified glass-ionomer cements". An Introduction to Dental Materials (4th ed.). London: Elsevier/Mosby. pp. 95-106. ISBN 978-0-7234-3659-1. OCLC 821697096.
- Powers, John M.; John C. Wataha (2013). Dental Materials: Properties and Manipulation (10th ed.). St. Louis, Mo.: Elsevier/Mosby. ISBN 978-0-323-07836-8. OCLC 794161326.
- Wilson, A. D.; J. W. Nicholson (2005) [1993]. "5.9 Glass polyalkenoate (glass-ionomer) cement". Acid-Base Cements: Their Biomedical and Industrial Applications. Chemistry of Solid State Materials 3 (reprint ed.). Cambridge, UK: Cambridge University Press. pp. 116-196. ISBN 978-0-521-67549-9. OCLC 749544621. Retrieved 28 March 2013.
- Wilson, Alan D.; John W. McLean (1988). Glass-ionomer Cement. Chicago: Quintessence Publishing Company. ISBN 978-0-86715-200-5. OCLC 17300425.
Source of the article : Wikipedia